We report on the growth and characterization of SrRuO3 single layers and SrRuO3/SrTiO3/SrRuO3 heterostructures grown on SrTiO3(100) substrates. The thickness dependence of the coercivity was determined for these single layers. Heterostructures with barrier thickness tb=1, 2.5, and 4 nm were fabricated, with electrodes having thickness ranging from 10 to 100 nm. The hysteresis loops of heterostructures with tb=2.5¿nm, 4 nm reveal uncoupled magnetic switching of the electrodes. Therefore, these heterostructures can be used for the fabrication of magnetic tunneling junctions.